par Dibazar, Zahra Ebrahimvand;Mohammadpour, Mahnaz;Samadian, Hadi;Zare, Soheila;Azizi, Mehdi;Hamidi, Masoud
;Elboutachfaiti, Redouan;Petit, Emmanuelle;Delattre, Cédric
Référence Materials, 15, 7, 2494
Publication Publié, 2022-04
![](/vufind/images/ULB/publications_list.png)
Référence Materials, 15, 7, 2494
Publication Publié, 2022-04
Article révisé par les pairs
Résumé : | 3D nanocomposite scaffolds have attracted significant attention in bone tissue engineering applications. In the current study, we fabricated a 3D nanocomposite scaffold based on a bacterial polyglucuronic acid (PGU) and sodium alginate (Alg) composite with carbon nanofibers (CNFs) as the bone tissue engineering scaffold. The CNFs were obtained from electrospun polyacrylonitrile nanofibers through heat treatment. The fabricated CNFs were incorporated into a PGU/Alg polymeric solution, which was physically cross-linked using CaCl2 solution. The fabricated nanocomposites were characterized to evaluate the internal structure, porosity, swelling kinetics, hemocompatibility, and cytocompatibility. The characterizations indicated that the nanocomposites have a porous structure with interconnected pores architecture, proper water absorption, and retention characteristics. The in vitro studies revealed that the nanocomposites were hemocompatible with negligible hemoly-sis induction. The cell viability assessment showed that the nanocomposites were biocompatible and supported bone cell growth. These results indicated that the fabricated bacterial PGU/Alg/CNFs hydrogel nanocomposite exhibited appropriate properties and can be considered a new biomaterial for bone tissue engineering scaffolds. |