Wireless Addressing of Freestanding MoSe2 Macro- and Microparticles by Bipolar Electrochemistry

par Malytska, Iuliia;Doneux, Thomas ;Bougouma, Moussa;Kuhn, Alexandre;Bouffier, L.
Référence The Journal of Physical Chemistry Part C: Nanomaterials and Interfaces, 123, 9, page (5647-5652)
Publication Publié, 2019-10-01

Article révisé par les pairs

• Accès en ligne
• Détails
• Contenu
• Statistiques

Résumé :

Doping of a transition-metal dichalcogenide deposited onto a conducting surface acting as bipolar electrode was recently reported. Here, freestanding macro- and microscale transition-metal dichalcogenide substrates are successfully employed as effective bipolar electrodes without the need of using an additional conducting support. This is first demonstrated by achieving site-selective bipolar electrodeposition of several metals, such as gold, silver, copper, and nickel, on macroscale MoSe 2 substrates (typically 1 mm in size). Also, the superior efficiency of MoSe 2 compared to that of a carbon substrate toward hydrogen evolution reaction, well-known in conventional electrochemistry, is demonstrated in the bipolar electrochemistry configuration. Such electrocatalytic properties can be advantageously used by combining this reduction with a given oxidation reaction to ease the electrochemical coupling. Also, as a wireless technique, bipolar electrochemistry enables the simultaneous addressing of large ensembles of bipolar electrodes with a single pair of driving electrodes. Therefore, in a bulk experiment, a suspension composed of thousands of individual MoSe 2 microparticles (with a typical size of 20-80 μm) that are addressed simultaneously, is employed to significantly accelerate electrolysis. Amplex Red was selected as an oxidizable organic model dye. Such electrolysis occurs on the timescale of several seconds, which is definitely not achievable by addressing a single macroscale MoSe 2 bipolar electrode. This performance is due to the collective behavior of the ensemble of MoSe 2 bipolar electrodes because the oxidation process occurs simultaneously at each individual anodic pole.