Structural/textural properties and water reactivity of fluorinated activated carbons

par Parmentier, Julien;Schlienger, Sébastien;Dubois, Marc Alexandre;Disa, Elodie;Masin, Francis ;Centeno, Teresa T.A.
Référence Carbon, 50, 14, page (5135-5147)
Publication Publié, 2012-11

Article révisé par les pairs

• Accès en ligne
• Détails
• Contenu
• Statistiques

Résumé :

Hydrophobic activated carbons are considered as interesting materials for air or water remediation due to their enhanced affinity for slightly water-soluble organic species. In this context, a commercial activated carbon, in an extruded form, was fluorinated under mild conditions (pure fluorine gas at room temperature) in order to decrease its hydrophilic character and to preserve its microporosity. For comparison, a hydrogenated activated carbon was also prepared by H 2 treatment. The resulting samples were characterised by various techniques in order to determine the evolution of the activated carbon materials in terms of composition (XPS, elemental analysis, TGA and NMR) and porosity (nitrogen physisorption (77 K), mercury intrusion and immersion calorimetry). For the fluorinated carbon, the nature of the CF x groups and the strength of the C-F bonds were also investigated using 13C and 19F solid state NMR and TGA techniques. A labile character of the C-F bond, so far exclusively observed for fluorine intercalation compounds, is also shown for the first time for a fluorinated activated carbon by water adsorption/desorption isotherms at room temperature. Care should then be taken for its use in presence of water. © 2012 Elsevier Ltd. All rights reserved.